| Title: | Avaliação da estabilidade da Resistência de União (RU) de diferentes materiais utilizados para o reparo de coroas impressas em resina 3D |
| Other Titles: | Evaluation of the stability of Shear bond Strength (SBS) of different materials for repairing 3D-printed resin crowns |
| Authors: | Silva, Raquel Cardoso da |
| Orientador(es):: | Garcia, Fernanda Cristina Pimentel |
| Coorientador(es):: | Medeiros, Rodrigo Antônio de |
| Assunto:: | Restauração temporária (Odontologia) Impressão 3D Resinas dentárias |
| Issue Date: | 25-Sep-2024 |
| Data de defesa:: | 3-Jul-2024 |
| Citation: | SILVA, Raquel Cardoso da. Avaliação da estabilidade da Resistência de União (RU) de diferentes materiais utilizados para o reparo de coroas impressas em resina 3D. 2024. 61 f., il. Dissertação (Mestrado em Odontologia) — Universidade de Brasília, Brasília, 2024. |
| Abstract: | As restaurações provisórias são utilizadas para manter a estética e função durante a confecção de restaurações indiretas. Elas estão sujeitas a tensões mastigatórias da cavidade bucal e podem sofrer fraturas, desgastes, entre outras condições que indiquem o procedimento de reparo. Diante disso, o objetivo desse estudo foi avaliar a Resistência de União (RU) de 4 materiais utilizados em reparos de coroas provisórias produzidas por impressão em 3D imediatamente e após a termociclagem. A interface adesiva foi avaliada pelo teste de cisalhamento realizado em máquina de ensaio universal, com célula de carga de 5 KN, em uma velocidade de 0,5 mm /min .Foram confeccionados 16 discos cilíndricos em resina para impressão 3D de coroas provisórias (18 x3 mm),tendo a superfície polida, em seguida foram realizados reparos (RODs) utilizando quatro resinas diferentes (n=8/cada tempo) : Resina Acrílica Autopolimerizável (GA) – Dêncor (Clássico – Brasil), Resina Bisacrílica (GB) – Primma Art (FGM – Brasil), Resina Flow (GFF) – Opallis (FGM – Brasil) e Resina Flow (GFS) – Beautifil Injectable XSL (Shofu – Japão) e avaliados após 24 hs (T0) ou após 10000 ciclos de termociclagem (T1) e submetidos ao teste de cisalhamento. O tipo de falha na interface adesiva foi avaliada. Os dados obtidos de Resistência de União (MPa) foram submetidos à análise de Variância (ANOVA) de dois fatores (material de reparo e tempo) seguido do teste de Tukey, (p<0.05). Houve interação entre os fatores avaliados (p<0,001). Em T0 e T1, o grupo GFS apresentou os maiores valores de RU com diferença estatística significativa para os demais grupos GFF, GB e GA que diferiram entre si (p<0,05) . Os valores de RU diminuíram após a termociclagem para cada material (p<0,05) exceto para o GA (p>0,05). Observou-se que o tipo de material de reparo e o tempo influenciaram nos valores de RU A Resina Flow (GFS) pode ser o material mais indicado para o reparo de coroas provisórias confeccionadas com a resina para impressão 3D avaliada. |
| Abstract: | Temporary restorations play a crucial role in maintaining both aesthetics and functionality during the fabrication of indirect restorations.These restorative materials are subjected to masticatory forces within the oral cavity, making them susceptible to fractures, wear, and other conditions that may necessitate repair. This work aimed to evaluate the Shear bond Strength (SBS) of four different materials used for repairing temporary crowns produced through 3D printing both immediately and following thermocycling. The adhesive interface was evaluated by a shear test performed on a universal testing machine, with a 5 KN load cell, at a speed of 0.5 mm/min. Sixteen cylindrical discs (18 x 3 mm) were produced using 3D printing resin specifically designed for temporary crowns, with repairs (RODs) performed using four different resins (n=8/ for each time): Auto-Polymerizing Acrylic Resin (GA) - Dêncor (Clássico – Brazil), Bis-Acrylic Resin (GB) - Primma Art (FGM – Brazil), Flow Resin (GFF) - Opallis (FGM – Brazil), and Flow Resin (GFS) – Beautifil Injectable XSL (Shofu – Japan). The specimens were evaluated after 24 hours (T0) and after undergoing 10,000 thermocycling cycles (T1). Prior to repair, the surfaces of the printed resins were polished to ensure optimal bonding.. The samples were stored in distilled water for 24 hours at 37°C or subjected to thermocycling before shear testing . The type of adhesive failure was evaluated. Shear bond strength data (MPa) were analyzed using two-way Analysis of Variance (ANOVA) (repair material and time), followed by Tukey's post-hoc ttest (p<0.05). A significant interaction between the evaluated factors was identified (p<0.001). At both T0 and T1, the GFS group exhibited superior SBS values with statistically significant differences compared to the other groups (GFF, GB, and GA), which differed from each other (p<0.05). SBS values decreased following thermocycling for each material (p<0.05) except for GA (p>0.05). This study highlights that both the type of repair material and the time factor significantly influence SBS values. Among the materials tested, Flow Resin (GFS) appears to be the most suitable for repairing temporary crowns fabricated from the evaluated 3D printed resin. |
| metadata.dc.description.unidade: | Faculdade de Ciências da Saúde (FS) |
| Description: | Dissertação (mestrado) — Universidade de Brasília, Faculdade de Ciências da Saúde, Programa de Pós-Graduação em em Odontologia, 2024. |
| metadata.dc.description.ppg: | Programa de Pós-Graduação em Odontologia |
| Licença:: | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.unb.br, www.ibict.br, www.ndltd.org sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra supracitada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data. |
| Appears in Collections: | Teses, dissertações e produtos pós-doutorado |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.