Título :	Evaluation of mechanical properties and microstructure of high-performance mortars with superabsorbent polymers and metakaolin by means of X-ray computed microtomography
Autor :	Silva, Arthur Aviz Palma e Capuzzo, Valdirene Maria Silva C. Silva, Eugênia Fonseca Pereira, André Maues Brabo Silva, Douglas Aviz Palma e
metadata.dc.contributor.affiliation:	University of Brasília, Graduate Program in Structures and Civil Construction University of Brasília, Graduate Program in Structures and Civil Construction University of Brasília, Graduate Program in Structures and Civil Construction Federal Fluminense University State University of Pará
Assunto::	Polímero superabsorvente Concreto de alto desempenho Microtomografia de raios X
Fecha de publicación :	feb-2022
Editorial :	lsevier Ltd.
Citación :	SILVA, Arthur Aviz Palma e et al. Evaluation of mechanical properties and microstructure of high-performance mortars with superabsorbent polymers and metakaolin by means of X-ray computed microtomography. Journal of Building Engineering, v. 51, 104219, 2022. DOI: https://doi.org/10.1016/j.jobe.2022.104219
Abstract:	Superabsorbent polymers (SAP) may provide internal curing in cementitious materials, conse- quently, they reduce autogenous shrinkage caused by low water/cement ratios and autodesse- cation of pores. This paper aimed to analyze the effect of Superabsorbent polymers in high- strength mortars, using metakaolin as supplementary cementitious material (SCM). A X-ray microtomography test was carried out on two mixtures of mortars, a reference mix (MKREF) and a mix containing 0.30% superabsorbent polymer (MKSAP30), and the acquired images enabled the evaluation of mortar phases, anhydrate cement and void content. Also, a compressive strength test was carried out at 3 ages for both mixtures. The superabsorbent polymer was added still dry in the mixture, and no extra water was used for SAP absorption, hence, all the mixtures had the same total water/cement ratios. The results point to an increase in mechanical properties on mortars modified with SAP of 51% at the age of 28 days. Also, a higher porosity was observed in MKSAP30 samples, however, the pores were of small diameters, showing that SAP may provide refinement in pores of the cement matrix. In addition, a higher pore connectivity was detected, and an increase in the number of pores accounted using microtomographic images and the software called Fiji/ImageJ software for MKSAP30. The SAP modified mortar also showed more pores tortuosity. Finally, a lower percentage of anhydrate cement remaining in the mixture with SAP was shown, pointing to an optimization of the hydration degree, corroborating to the improvement of mechanical properties.
metadata.dc.description.unidade:	Faculdade de Tecnologia (FT) Departamento de Engenharia Civil e Ambiental (FT ENC)
metadata.dc.description.ppg:	Programa de Pós-Graduação em Estruturas e Construção Civil
DOI:	https://doi.org/10.1016/j.jobe.2022.104219
metadata.dc.relation.publisherversion:	https://www.sciencedirect.com/science/article/pii/S2352710222002327?via%3Dihub
Aparece en las colecciones:	Artigos publicados em periódicos e afins

Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.