Título :	The influence of potassium hydroxide concentration and reaction time on the extraction cellulosic jute fibers
Autor :	Kataoka, Lays Furtado de Medeiros Souza Hidalgo Falla, Maria Del Pilar Luz, Sandra Maria da
metadata.dc.identifier.orcid:	https://orcid.org/ 0000-0003-1766-7509 https://orcid.org/ 0000-0002-2223-0021
Assunto::	Alfa celulose Holocelulose Fibra de juta Planejamento fatorial Alcalinização Propriedades térmicas
Fecha de publicación :	8-jun-2021
Editorial :	Taylor & Francis
Citación :	KATAOKA, Lays Furtado de Medeiros Souza; HIDALGO FALLA, Maria Del Pilar; Luz, Sandra Maria da. The influence of potassium hydroxide concentration and reaction time on the extraction cellulosic jute fibers. Journal of Natural Fibers, 2021. DOI: https://doi.org/10.1080/15440478.2021.1934934.
Abstract:	A common method used to obtain cellulosic fibers is alkalinization with NaOH. Depending on NaOH content, treatments remove significant quantities of lignin and hemicellulose as small molecules. In biorefineries, where the preservation of components is needed, KOH may prevent hemicellulose chain formation. Here, we studied the efficacy of obtaining cellulosic fibers from jute using KOH. Jute fibers are about 84.2% holocellulose, which corresponds to 59.5% alpha cellulose and 24.7% hemicellulose. To obtain high cellulosic fiber yields from jute, effects of pulping with different KOH concentrations and altering reaction times were studied using factorial planning (22). Afterward, in natura and treated fibers were characterized via Fourier transform infrared spectroscopy (FTIR), thermogravimetry (TG) and derivative thermogravimetry. Holocellulose sample components were obtained by removing lignin. Factors including concentration and reaction time individually significantly affected cellulose yield. Alpha cellulose was produced when higher levels of the factorial planning conditions were applied. Ideal parameters for cellulose extraction included the addition of 10% (w/v) KOH for 3 h. FTIR analysis was used to ensure that lignocellulosic components were removed by fiber treatment. TG showed that treated fibers were thermally stable at temperatures close to, or higher than, in natura fibers.
metadata.dc.description.unidade:	Faculdade UnB Gama (FGA)
DOI:	https://doi.org/10.1080/15440478.2021.1934934
metadata.dc.relation.publisherversion:	https://www.tandfonline.com/doi/full/10.1080/15440478.2021.1934934
Aparece en las colecciones:	Artigos publicados em periódicos e afins

Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.